Synthesis and electrochemical characteristics of Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials for lithium ion batteries

LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials have been coated with Al₂O₃ nano-particles using sol-gel processing to improve its electrochemical properties. The X-ray diffraction (XRD) pattern of the as-prepared Al₂O₃ nano-particles was indexed to the cubic structure of the γ-Al₂O₃ phase and had an average size of ∼4 nm. The XRD showed that the structure of LiNi_1/3Co_1/3Mn_1/3O₂ was not affected by the Al₂O₃ coating. However, the Al₂O₃ coatings on LiNi_1/3Co_1/3Mn_1/3O₂ improved the cyclic life performance and rate capability without decreasing its initial discharge capacity. These electrochemical properties were also compared with those of LiAlO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ cathode material. The electrochemical impedance spectroscopy (EIS) was studied to understand the enhanced electrochemical properties of the Al₂O₃-coated LiNi_1/3Co_1/3Mn_1/3O₂ compared to uncoated LiNi_1/3Co_1/3Mn_1/3O₂.     

聚氯乙烯弹性体气候老化性能研究

将聚氯乙烯(PVC)弹性体试样进行户外曝晒试验,对试样老化前后的外观、力学性能、扫描电镜、红外光谱等试验结果进行分析比较,考察了光、热、氧对PVC弹性体气候老化性能的影响。研究结果表明:曝晒6个月后PVC的外观暗淡但有韧性,出现少量裂纹,分布也不均匀;拉伸强度逐渐增加,而断裂伸长率逐渐下降,16个月时下降到73.26%。导致断裂伸长率下降和拉伸强度逐渐增加的原因是DOP增塑剂的慢慢挥发。PVC样品经过16个月的曝晒后的红外光谱显示:波峰1620cm-1的出现说明有C=C存在,波峰969cm-1的消失说明高分子中的CH2断裂,这些都是分子老化所造成的。最后通过数学建模应用软件计算16个月后的断裂伸长率,预测可知:PVC弹性体在户外暴露30个月后就失去使用价值。     

一种基于随机GA的提高BP网络泛化能力的方法

LM-BP网络对其初始权值和阈值敏感,泛化能力不强,针对该缺点,采用遗传算法（GA）对其初始权阈值进行优化,在一定程度上能提高LM-BP网络的泛化能力。为进一步扩展GA初始种群的覆盖范围,进一步提高LM—BP网络的泛化能力,采用多次随机产生初始种群多次优化的方法。以伦河孝感段氟化物含量为实例,建立随机GA的LM—BP网络模型,对原始数据进行拟合及测试,结果表明该方法基本能100％拟合,测试误差不超过2．3％。经过对比实验,证明了该方法的有效性。     

银型抗菌沸石的合成

沸石类抗菌材料是一种无机多功能材料，具有耐酸，耐碱，过滤除污，吸附除臭以及长效广泛的杀菌和抑菌效果，主要介绍液相，固相离子交换法将具有抗菌性能的银离子与沸石合成为抗菌沸石，用正交法确定两种方法的较佳条件，并进行比较，用红外光谱对沸石原样与抗菌沸石进行比较分析，同时对合成的抗菌沸石进行了抗菌性能测试。     

气—液传质设备浮阀复合塔板的应用

介绍气～液传质设备中浮阀复合塔板的应用情况，采用浮阀复合塔板可在尽可能不降低板效率的同时提高塔器的生产能力。     

Activated carbon fiber cloths as electrodes for high performance electric double layer capacitors

Activated carbon fiber cloth (ACFC) electrodes with high double layer capacitance and good rate capability were prepared from polyacrylonitrile (PAN) fabrics by optimizing the carbonization temperature prior to CO₂ activation. The carbonization temperature has a marked effect on both the pore structure and the electrochemical performances of the ACFCs. Moderate carbonization at 600 °C results in higher specific surface area and larger pore size, and hence higher capacitance and better rate capability. The specific capacitance of the ACFCs in 6 mol L⁻¹ KOH aqueous solution can be as high as 208 F g⁻¹. It remains 129 F g⁻¹ as the current density increases to 10 000 mA g⁻¹.     

银系无机抗菌剂的研究进展

本文综述了银系无机抗菌剂的抗菌机理，类型，制备工艺和应用现状及其抗菌性能评价的方法，探讨了银系无机抗菌剂的发展趋势。     

面向能力组件的项目管理系统研究

当前企业面临的多项目管理环境日益突出,如何结合管理创新,搭建有效的项目管理平台,支撑多项目目标实现是众多企业面临的突出问题。文章结合装备研制,分析了多项目环境下传统管理方式存在的不足,提出了能力组件和计划视图的概念,构建了一种基于能力组件的项目管理方法和分级计划管理模型,设计并开发了面向能力组件的项目管理系统。详细说明了系统的技术架构、功能组成和关键技术,并结合应用实践,介绍了一种基于能力组件的项目管理组织模式和计划制定过程。     

双层模糊系统融合中心约束型最小包含球

与传统的TSK模糊系统相比,改进的双层TSK模糊系统CTSK(Central TSK Fuzzy System)有如下优点:良好的可解释性、更好的鲁棒性、较强的逼近能力。但对于大样本或超大样本数据集,其时间复杂度和空间复杂度的开销都极大地限制了它的实用性。针对此不足,通过模糊系统融合中心约束型最小包含球(CCMEB)理论提出了CCMEB-CTSK(CCMEB-based CTSK)算法。该算法在继承CTSK优点的同时,又较好地实现了处理大样本和超大样本数据集的有效性和快速性。仿真实验研究分析了采用不同模糊规则数的CCMEB-CTSK的性能指标和运行时间的比较,以及训练样本不加噪声和加入噪声情况下CCMEB-CTSK泛化能力和鲁棒性能的测试。     

面向移动互联网的OSS服务能力开放架构设计与应用

在移动互联网环境下,实现OSS服务能力开放是增强电信企业运营支撑能力、提升客户感知的重要手段。从OSS服务能力开放需求分析入手,提出面向移动互联网的OSS服务能力开放架构,并通过实际业务场景进行验证。